specification ? supplier : samsung electro-mechanics ? samsung p/n : CL21A226MPCLRNC ? product : multi-layer ceramic capacitor ? description : cap, 22 ? , 10v, 20%, x5r, 0805 cl 21 a 226 m p c l r n c ? ???? series samsung multi-layer ceramic capacitor size 0805 (inch code) l: 2.0 0.2 mm w: 0.2 mm thickness division low profile dielectric x5r inner electrode capacitance 22 ? termination capacitance 20 % plating (pb free) tolerance product l,w size tolerance change code rated voltage 10 v special reserved for future use thickness 0.85 0.1 mm ? packaging cardboard type, 7"reel(4,000ea) a. samsung part number 1.25 ni cu sn 100% b. samsung reliability test and judgeme nt condition capacitance within specified tolerance 120 ? 20% 0.50.1vrms tan (df) 0.1 max. insulation more than 100mohm ? ? rated voltage 60~120 sec. resistance appearance no abnormal exterior appearance visual inspection withstanding no dielectric breakdown or of the rated voltage voltage mechanical breakdown temperature x5r characteristics (from -55 to 85 , capacitance change should be within 15%) adhesive strength no peeling shall be occur on the 500g ? f, for 101 sec. of termination terminal electrode bending strength capacitance change : within 12.5% bending to the limit (1mm) with 1.0mm/sec. solderability more than 75% of terminal surface snag3.0cu0.5 solder is to be soldered newly 2455 , 30.3sec. (preheating : 80~120 for 10~30sec.) resistance to capacitance change : within 7.5% solder pot : 2705 , 101sec. soldering heat tan , ir : initial spec. 250% performance test condition
vibration test capacitance change : within 5% amplitude : 1.5mm tan , ir : initial spec. from 10 ? to 55 ? (return : 1min.) 2hours ? 3 direction (x, y, z) moisture capacitance change : within 12.5% with rated voltage resistance tan : 0.2 max 402 , 90~95%rh, 500+12/-0 hour ir : more than 12.5 ? ? high temperature capacitance change : within 12.5% wit h of the rated voltage resistance tan : 0.2 max max. operating temperature ir : more than 25 ? ? 1000+48/-0 hour temperature capacitance change : within 7.5% 1 cycle condition cycling tan , ir : initial spec. min. operating temperature 25 max. operating temperature 25 5 cycles test c. recommended soldering method : reflow ( reflow peak temperature : 260+0/-5 , 10sec. max ) * for the more detail specification, please refer to the samsung mlcc catalogue. performance test condition 100%
|